1. Ka laulā a me ka hoʻokaʻawale

Ke Kaʻina Hana Hana: E pili ana i nā paipu kila welded e like me ka uila kū'ē kū'ē (ERW) a me ka submerged arc welding (SAW).

Hoʻokaʻawale: Hoʻokaʻawale ʻia i ka Papa A (pae kumu) a me ka Papa B (pae kiʻekiʻe) e like me ke koʻikoʻi o ka nānā ʻana. Hāʻawi ʻia ʻo P355NH ma ke ʻano he papa B.

2. Nā Kūlana Hoʻouna Nui

Ka maikaʻi o ka ʻili: ʻAʻohe hemahema e like me nā māwae a me nā pelu. ʻAe ʻia ka unahi oxide liʻiliʻi (ʻaʻole pili i ka nānā ʻana).

Makaʻala: Pono e kaha ʻia kēlā me kēia paipu kila me ka helu maʻamau, ke kila kila (P355NH), ka nui, ka helu umu, a me nā mea ʻē aʻe (EN 10217-1).

Ka hoʻomanawanui ana (EN 10217-1)

ʻĀpana	Nā koi hoʻomanawanui papa B (pili iā P355NH)	ʻano hoʻāʻo (EN)
Anawaena waho (D)	±0.75% D a i ʻole±1.0mm (ka waiwai nui)	EN ISO 8502
Mānoanoa pā (t)	+10%/-5% t (t≤15mm)	Ana mānoanoa ultrasonic (EN 10246-2)
Ka lōʻihi	+100/-0 mm (lōʻihi paʻa)	ʻO ka pae laser

 

Nā kikoʻī kaʻina hana nui o ka paipu kila P355NH

1. Hoʻomalu kaʻina hana kuʻi (EN 10217-3)

paipu kila ERW:

Pono ka hoʻomaʻamaʻa wela ma ka pūnaewele ma hope o ka welding kiʻekiʻe (hoʻomehana induction i 550 ~ 600℃a me ka hooluolu lohi).

Weld seam extrusion mana:≤10% ka mānoanoa o ka paia (e pale i ka hui ʻole ʻana). 

SAW paipu kila: 

ʻO ka hoʻoheheʻe ʻana i nā uea he nui (2 ~ 4 uea), hoʻokomo wela≤35 kJ/cm (no ka pale ʻana i ka palaoa HAZ). 

1. Nā kikoʻī o ka mālama wela (EN 10217-3 + EN 10028-3)

Kaʻina hana	nā palena	Ke kumu
Hana maʻamau (N)	910±10℃×1.5min/mm, hoʻoluʻu ea	E hoʻomaʻemaʻe i nā kīʻaha i ka papa ASTM 6~8
Hoʻopiʻi hoʻomaha hoʻoluhi (SR)	580~620℃×2min/mm, hoʻoluʻu umu (≤200℃/h)	Hoʻopau i ke koʻikoʻi koena wili

3. ʻO ka hoʻāʻo ʻana ʻole (EN 10217-1 + EN 10217-3)

Hoʻāʻo UT:

ʻIkepili:Φ3.2mm puka papa lalo (EN ISO 10893-3). 

Ka uhi: 100% weld + 10mm makua mea ma nā ʻaoʻao ʻelua. 

ʻO ka hoʻāʻo kaomi wai: 

Pumi hoao = 2×ʻae ʻia ke kaomi hana (ka liʻiliʻi 20MPa, paʻa paʻa≥15s).

Nā koi hoʻohui no nā noi kūikawā

1. Haʻahaʻa wela hopena ʻoʻoleʻa (-50℃)

Nā ʻōlelo ʻaelike hou:

Ka ikehu hopena≥60J (awelika), hoʻokahi kikoʻī≥45J (EN ISO 148-1). 

E hoʻohana i ke kaʻina hana deoxidation composite Al+Ti e hōʻemi i ka ʻike oxygen (≤30ppm). 

2. Ka ikaika hoʻomanawanui wela kiʻekiʻe (300℃)

Ho'āʻo hou:

10^5 mau hola kolo rupture ikaika≥150 MPa (ISO 204).

Kiʻekiʻe wela tensile ʻikepili (Rp0.2@300℃≥300 MPa) pono.

3. Nā koi kū'ē i ka corrosion

Kaʻina hana koho:

ʻO ke kiʻi ʻana o ka pā o loko (Sa 2.5 pae, EN ISO 8501-1).

Hoʻopili ʻia ka pā o waho me Zn-Al alloy (150g/m², Annex B o EN 10217-1).

Nā Palapala Kūlana a me ka palapala hōʻoia (EN 10217-1)

Palapala Nānā:

EN 10204 3.1 Palapala (nā mea kanu hao hao) a i ʻole 3.2 palapala (hōʻoia ʻekolu ʻaoʻao).

Pono e komo i loko o: haku mele kemika, waiwai mekini, nā hualoaʻa NDT, ka pihi hoʻomaʻamaʻa wela.

Hoailona kūikawā:

Hōʻailona ʻia nā paipu haʻahaʻa haʻahaʻa me "LT" (-50℃). 

Hōʻailona ʻia nā paipu wela wela me ka "HT" (+300℃).

Nā pilikia maʻamau a me nā hoʻonā

Pilikia Phenomenon	Nānā Kumu	Nā Hoʻoponopono (Ma muli o nā Kūlana)
ʻAʻole lawa ka ikehu hopena o ka welds	nā huaʻai HAZ koʻikoʻi	hoʻololi i ka hoʻokomo wela welding≤25 kJ/cm (EN 1011-2)
Leaka hoʻāʻo hydraulic	Nā ʻāpana mīkini hoʻopololei kūpono ʻole	Ka nānā hou ʻana o UT i ka ʻāpana paipu holoʻokoʻa + ka nānā ʻana i ka radiographic kūloko (EN ISO 10893-5)
Hoʻokaʻawale ana (ovality)	Nā ʻāpana mīkini hoʻopololei kūpono ʻole	Hoʻopololei hou (EN 10217-1)

Ma ka hoʻohui ʻana i nā ʻōlelo maʻamau o BS EN 10217-1 me nā koi kūikawā o BS EN 10217-3, hiki ke hoʻomalu piha ʻia ka maikaʻi o ke kaʻina holoʻokoʻa o ka paipu kila P355NH mai ke koho ʻana i nā mea a hiki i ka ʻae ʻana i ka huahana. I ke kūʻai ʻana, manaʻo ʻia e haʻi pololei i ka mana maʻamau (e like me BS EN 10217-3:2002+A1:2005) a me nā ʻaelike loea hou (e like me -50℃nā koi hopena) ma ka ʻaelike.