nòt 1: tout dat la se pi plis valè.

nòt 2: "—" vle di pa gen okenn demann

① "W" vle di Fitting pou konekte.

② lè Fitting an se baton ak plak, pi C a ta dwe 0.35

③ Fittings yo fòje ki pi C a se 0.35. ak pifò Si se 0.35 epi pa gen limite pou minimòm

④ lè C a pi ba pase demann pi ba a, C diminye 0.01% epi Mn ap ogmante 0.06%, jouk nan pifò Mn se 1.35%

⑤ Cu, Ni Cr Mo total mwens pase 1.00%

⑥ 0.32%。Cr Mo total mwens pase 0.32%

⑦ analiz chalè ak analiz final pwodwi yo pral tou de apwopriye.

Voye imèl ba nou Telechaje kòm PDF

Pwodwi detay

Tags pwodwi

Nou kenbe prensip "bon jan kalite pou kòmanse, sèvis okòmansman, amelyorasyon kontinyèl ak inovasyon pou satisfè kliyan yo" pou administrasyon ou ak "zewo defo, zewo plent" kòm objektif estanda. Pou kokenn sèvis nou an, nou ofri pwodwi yo lè l sèvi avèk bon jan kalite a trè bon nan pri a rezonab pou pi bon pri sou P5 P9 orè 80 tiyo asye galvanised ak sètifika IBR ki te pibliye pa TUV, Tout machandiz rive ak bon jan kalite segondè ak gwo pwodwi apre-lavant ak sèvis yo. Mache-oryante ak kliyan-oryante se sa nou te yo te imedyatman apre. Sensèman antisipe Win-Gen koperasyon!
Nou kenbe prensip "bon jan kalite pou kòmanse, sèvis okòmansman, amelyorasyon kontinyèl ak inovasyon pou satisfè kliyan yo" pou administrasyon ou ak "zewo defo, zewo plent" kòm objektif estanda. Pou kokenn sèvis nou an, nou ofri pwodwi yo lè l sèvi avèk bon jan kalite a trè bon nan pri a rezonab poubv sètifika, ibr, P5 alyaj tiyo, P9 alyaj tiyo, Sètifika Tuv, Konsepsyon an, pwosesis, achte, enspeksyon, depo, pwosesis rasanble yo tout nan pwosesis dokimantè syantifik ak efikas, ogmante nivo itilizasyon ak fyab nan mak nou an pwofondman, ki fè nou vin founisè siperyè nan kat gwo kategori pwodwi koki depoze domestik ak jwenn konfyans kliyan an byen.

ASME SA-234/SA-234M

NO	Klas ①	% konpozan chimik																	Pwopriyete mekanik
		C	Mn	P	S	Si	Cr	Mo	Ni	Cu	V	Nb	N	Al	Ti	Zr	W	B	Tensile MPa	Sede MPa	Pwolonje L/T	handness HB

1	WPB ②③④⑤⑥	≤0.30	0.29- 1.06	≤ 0.050	≤ 0.058	≥ 0.10	≤ 0.40	≤ 0.15	≤ 0.40	≤ 0.40	≤ 0.08	—	—	—	—	—	—	—	415- 585	≥240	22/14%	≤ 197
2	WPC ③④⑤⑥	≤ 0.35	0.29- 1.06	≤ 0.050	≤ 0.058	≥ 0.10	≤ 0.40	≤ 0.15	≤ 0.40	≤ 0.40	—	≤ 0.08	—	—	—	—	—	—	485- 655	≥ 275	22/14%	≤ 197
3	WP1	≤ 0.28	0.30- 0.90	≤ 0.045	≤ 0.045	0.10- 0.50	—	0.44- 0.65	—	—	—	—	—	—	—	—	—	—	380- 555	≥205	22/14%	≤ 197
4	WP12 1	0.05- 0.20	0.30- 0.80	≤ 0.045	≤ 0.045	≤ 0.60	0.80- 1.25	0.44- 0.65	—	—	—	—	—	—	—	—	—	—	415- 585	≥220	22/14%	≤ 197
	WP12 2																		485- 655	≥275	22/14%	≤ 197
5	WP11 1	0.05- 0.15	0.30- 0.60	≤ 0.030	≤ 0.030	0.50- 1.00	1.00- 1.50	0.44- 0.65	—	—	—	—	—	—	—	—	—	—	415- 585	≥205	22/14%	≤ 197
6	WP11 2	0.05- 0.20	0.30- 0.80	≤ 0.040	≤ 0.040	0.50- 1.00	1.00- 1.50	0.44- 0.65	—	—	—	—	—	—	—	—	—	—	485- 655	≥275	22/14%	≤ 197
	WP11 3																		520- 690	≥310	22/14%	≤ 197
7	WP22 1	0.05- 0.15	0.30- 0.60	≤ 0.040	≤ 0.040	≤ 0.50	1.90- 2.60	0.87- 1.13	—	—	—	—	—	—	—	—	—	—	415- 585	≥205	22/14%	≤ 197
	WP22 3																		520- 690	≥310	22/14%	≤ 197
9	WP9 1	≤0.15	0.30- 0.60	≤ 0.030	≤ 0.030	0.25- 1.00	8.0- 10.0	0.90- 1.10	—	—	—	—	—	—	—	—	—	—	415- 585	≥205	22/14%	≤ 217
	WP9 3																		520- 690	≥310	22/14%	≤ 217
10	WP91	0.08- 0.12	0.30- 0.60	≤ 0.020	≤ 0.010	0.20- 0.50	8.0- 9.5	0.85- 1.05	≤ 0.40	—	0.18- 0.25	0.06- 0.10	0.03- 0.07	≤ 0.02	≤ 0.01	≤ 0.01	—	—	585- 760	≥415	20/—%	≤ 248
11	WP911	0.09- 0.13	0.30- 0.60	≤ 0.020	≤ 0.010	0.10- 0.50	8.5- 9.5	0.90- 1.10	≤ 0.40	—	0.18- 0.25	0.06- 0.10	0.04- 0.09	≤ 0.02	≤ 0.01	≤ 0.01	0.90- 1.10	0.0003- 0.0006	620- 840	≥440	20/—%	≤ 248