API 5Lọkpọkọ ígwè nke pipeline
Ọkwa ígwè: L360 ma ọ bụ X52 (PSL1)
Ihe mejupụtara kemịkalụ chọrọ:
C: ≤0.28 (enweghị aka) ≤0.26 (agbadoro agbado)
Mn: ≤1.40
P: ≤0.030
S: ≤0.030
Cu: 0.50 ma ọ bụ ihe na-erughị
Nọmba: ≤0.50
Cr: ≤0.50
Ọnwa: ≤0.15
*V+Nb+Ti: ≤0.15
* Enwere ike ịbawanye ọdịnaya Manganese site na 0.05% maka mbelata ọ bụla 0.01% na ọdịnaya carbon, ruo oke kachasị nke 1.65%
Ihe achọrọ maka ihe onwunwe mekaniki:
Ike mmepụta: ≥360Mpa
Ike nrụgide: ≥460Mpa
Ike nrụgide nke ọkpọkọ ígwè a kpara akpa: ≥460Mpa
Ogologo: ≥1940* AXC0.2/4600.9, ebe AXC bụ mpaghara nkebi nke ihe nlele tensile
Nnwere onwe nke ọkpọkọ ígwè dị n'èzí:
| Dayameta mpụta D mm | Nkwụsị njedebe nke dayameta mpụga mm | |
| Paịpụ ígwè enweghị ntụpọ | Paịpụ ígwè a kpara agbatị | |
| < 60.3 | -0.8, +0.4 | |
| 60.3 D ma ọ bụ ihe na-erughị ya 168.3 ma ọ bụ ihe na-erughị ya | -0.4, +1.6 | |
| 168.3 < D≤610 | ±0.005D, mana kachasị ±1.6 | |
| 610 < D≤1422 | + / - 2.0 | + / - 1.6 |
| > 1422 | Site na nkwekọrịta | |
Mgbidi ọkpụrụkpụ ndidi of ígwè paịpụ:
| Ọkpụrụkpụ mgbidi t mm | Ndidi mm |
| Paịpụ ígwè enweghị ntụpọ | |
| 4.0 ma ọ bụ ihe na-erughị | +0.6, -0.5 |
| 4 < t < 25 | +0.150t, -0.125t |
| 25 ma ọ bụ karịa | +3.7 maọbụ +0.1t, nke ọbụla buru ibu -3.0 maọbụ -0.1t, were nke buru ibu karịa |
| Tube a gbanyere agbatị | |
| 5.0 ma ọ bụ ihe na-erughị | + / - 0.5 | |
| 5.0 | < t < 15 | Tụnyere ma ọ bụ mwepu 0.1 t |
| 15 | ma ọ bụ karịa | + / - 1.5 |
Ígwè ọkwa: L360N or X52N(PSL2)
Kemikal nhazi ihe ndị a chọrọ:
C: ≤0.24
Si: ≤0.45
Mn: ≤1.40
P: ≤0.025
S: ≤0.015
V: ≤0.10
Nb:≤0.05
Ti: ≤0.04
Cu: ≤0.50
Nọmba: ≤0.30
Cr: ≤0.30
Ọnwa: ≤0.15
V+Nb+Ti: ≤0.15
* Enwere ike ịbawanye ọdịnaya Manganese site na 0.05% maka mbelata ọ bụla 0.01% na ọdịnaya carbon, ruo oke kachasị nke 1.65%.
* Agaghị ekwe ka etinye boron n'ebumnobi, ihe fọdụrụ bụ B≤0.001%
Kabọn nhata:
CEP cm: ≤0.25
CEIIW: ≤0.43
* Jiri CE mgbe ọdịnaya carbon karịrị 0.12%, jiri CE IIW mgbe P cm ọdịnaya carbon erughị ma ọ bụ hà nhata 0.12%.
CEP cm = C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B
Ọ bụrụ na nsonaazụ nke nyocha ịgbaze B erughị 0.0005%, mgbe ahụ ọ dịghị mkpa itinye nyocha nke ihe B na nyocha ngwaahịa ahụ, a pụkwara iwere ọdịnaya B dị ka efu na ngụkọ CEP cm nke carbon.
CEIIW =C+Mn/6 (C+Mo+V)/5+(Ni+Cu)/ 15
Mekaniki ihe onwunwe ihe ndị a chọrọ:
Ike mmepụta: 360-530Mpa
Ike nrụgide: 460-760Mpa
Oke mmepụta: ≤0.93 (ọ dabara naanị na paịpụ ígwè D > 323.9mm)
Ike nrụgide nke ọkpọkọ ígwè a kpara akpa: ≥460Mpa
Ogologo kacha nta: = 1940* AXC0.2/4600.9, ebe AXC bụ mpaghara nkebi nke ihe nlele tensile.
Nnwale mmetụta CVN nke tube
Okpomọkụ ule 0 .C
| Dee dayameta mpụta nke D mm | CVN zuru okeIke a na-amịkọrọKVJ |
| 508 ma ọ bụ ihe na-erughị | 27 |
| > 508 ruo 762 | 27 |
| > 762 ruo 914 | 40 |
| > 914 ruo 1219 | 40 |
| > 1219 ruo 1422 | 40 |
| > 1422 ruo 2134 | 40 |
Mpụta dayameta ndidi of ígwè paịpụ:
| Dayameta mpụta D mm | Nkwụsị njedebe nke dayameta mpụga | |
| Paịpụ ígwè enweghị ntụpọ | Paịpụ ígwè a kpara agbatị | |
| < 60.3 | -0.4, +0.8 | |
| 60.3 D ma ọ bụ ihe na-erughị ya 168.3 ma ọ bụ ihe na-erughị ya | -0.4, +1.6 | |
| 168.3 < D=610 | ±0.005D, mana kachasị ±1.6 | |
| 610 < D=1422 | + / - 2.0 | + / - 1.6 |
| > 1422 | Site na nkwekọrịta | |
Mgbidi ọkpụrụkpụ ndidi of ígwè paịpụ:
| Ọkpụrụkpụ mgbidi t mm | Ndochi |
| Paịpụ ígwè enweghị ntụpọ | |
| 4.0 ma ọ bụ ihe na-erughị | +0.6, -0.5 |
| 4 < t < 25 | +0.150t, -0.125t |
| 25 ma ọ bụ karịa | +3.7 ma ọ bụ +0.1t, nke ọ bụla buru ibu -3.0 ma ọ bụ -0.1t, were nke ka ibu |
| Paịpụ a gbanyere agbatị | |
| 5.0 ma ọ bụ ihe na-erughị | + / - 0.5 |
| 5.0 < t < 15 | Tụnyere ma ọ bụ mwepu 0.1 t |
| Afọ 15 ma ọ bụ karịa | + / - 1.5 |