1. Oke na nhazi

Usoro Mmepụta: A na-etinye ya na ọkpọkọ ígwè e ji agbakọta dịka ịgbado ọkụ eletrik (ERW) na ịgbado ọkụ arc n'ime mmiri (SAW).

Nhazi: E kewara ya n'ime Klas A (ọkwa bụ isi) na Klas B (ọkwa dị elu) dịka nlezianya nke nyocha ahụ si dị. A na-enye P355NH dị ka Klas B.

2. Ọnọdụ Nnyefe Izugbe

Ogo Elu: Enweghị ntụpọ dịka mgbawa na mpịachi. A na-ekwe ka obere nha oxide (anaghị emetụta nyocha ahụ).

Akara: A ga-eji nọmba ọkọlọtọ, ọkwa ígwè (P355NH), nha, nọmba ọkụ, wdg. akara paịpụ ígwè ọ bụla (EN 10217-1).

Nnwere onwe nha (EN 10217-1)

Paramita	Ihe achọrọ maka ndidi Klas B (dị na P355NH)	Usoro nnwale (EN)
Dayameta mpụta (D)	±0.75% D ma ọ bụ±1.0mm (uru buru ibu)	EN ISO 8502
Ọkpụrụkpụ mgbidi (t)	+10%/-5% t (t≤15mm)	Nha ọkpụrụkpụ nke ultrasonic (EN 10246-2)
Ogologo	+100/-0 mm (ogologo a kapịrị ọnụ)	Usoro nhazi laser

 

Nkọwa usoro dị mkpa nke ọkpọkọ ígwè P355NH

1. njikwa usoro ịgbado ọkụ (EN 10217-3)

ERW ígwè ọkpọkọ:

A chọrọ ọgwụgwọ okpomọkụ n'ịntanetị mgbe ịgbado ọkụ ugboro ugboro (ọkụ induction ruo 550 ~ 600)℃na nwayọ nwayọ).

Njikwa mgbasa nke njikọta njikọta:≤Okpukpu mgbidi 10% (iji zere njikọta zuru oke). 

Paịpụ ígwè SAW: 

Ịgbado ọtụtụ waya (waya 2 ~ 4), ntinye okpomọkụ≤35 kJ/cm (iji gbochie mmebi nke ọka HAZ). 

1. Nkọwapụta ọgwụgwọ okpomọkụ (EN 10217-3 + EN 10028-3)

Usoro	paramita	Ebumnuche
Nhazi (N)	910±10℃×1.5min/mm, ikuku jụrụ oyi	Mee ka ọka ndị ahụ dị mma ka ọ bụrụ ọkwa ASTM 6-8
Mgbochi nrụgide (SR)	580~620℃×2 nkeji/mm, ọkụ oyi (≤200℃/h)	Wepụ nrụgide fọdụrụnụ nke ịgbado ọkụ

3. Nnwale na-adịghị emebi emebi (EN 10217-1 + EN 10217-3)

Nnwale UT:

Mmetụta uche:ΦOghere dị larịị nke dị 3.2mm (EN ISO 10893-3). 

Mkpuchi: 100% weld + ihe nne na nna 10mm n'akụkụ abụọ. 

Nnwale nrụgide mmiri: 

Nrụgide ule = 2×Nrụgide ọrụ a na-anabata (opekempe 20MPa, njide nrụgide≥15s).

Ihe ndị ọzọ achọrọ maka ngwa pụrụ iche

1. Ike mmetụta okpomọkụ dị ala (-50)℃)

Usoro nkwekọrịta ndị ọzọ:

Ike mmetụta≥60J (nkezi), otu ihe atụ≥45J (EN ISO 148-1). 

Jiri usoro Al+Ti nke mejupụtara deoxidation iji belata ọdịnaya oxygen (≤30ppm). 

2. Ike ntachi obi dị elu (300)℃)

Ule mgbakwunye:

Ike mgbawa nke awa 10^5≥150 MPa (ISO 204).

Data nrụgide okpomọkụ dị elu (Rp0.2@300)℃≥achọrọ 300 MPa).

3. Ihe achọrọ maka iguzogide nrụrụ aka

Usoro nhọrọ:

Mgbidi dị n'ime gbagburu peening (Sa 2.5 larịị, EN ISO 8501-1).

A na-eji ihe Zn-Al (150g/m2) kpuchie mgbidi mpụta ahụ², Mgbakwunye B nke EN 10217-1).

Akwụkwọ na Asambodo Dị Mma (EN 10217-1)

Asambodo Nnyocha:

Asambodo EN 10204 3.1 (nyocha onwe onye nke ụlọ ọrụ ígwè) ma ọ bụ Asambodo 3.2 (asambodo nke ndị ọzọ).

Ga-agụnyerịrị: ihe mejupụtara kemịkalụ, ihe ndị metụtara igwe, nsonaazụ NDT, usoro ọgwụgwọ okpomọkụ.

Akara pụrụ iche:

E ji akara "LT" (-50) akara paịpụ ndị dị ala maka okpomọkụ.℃). 

A na-eji akara "HT" (+300) akara paịpụ ndị dị elu℃).

Nsogbu na ngwọta ndị a na-ahụkarị

Nsogbu Ihe Na-eme	Nyocha Ihe Mere Ya	Ngwọta (Dabere na Ụkpụrụ)
Ike mmetụta zuru oke nke welds	mkpụrụ HAZ siri ike	gbanwee ntinye okpomọkụ ịgbado ọkụ≤25 kJ/cm (EN 1011-2)
Ntapu ule hydraulic	Paịmatị igwe na-ahazi nke ọma	Nnyocha ọzọ nke ngalaba paịpụ dum + nyocha redio mpaghara (EN ISO 10893-5)
Mgbanwe nha (ovality)	Paịmatị igwe na-ahazi nke ọma	Nhazigharị (EN 10217-1)

Site na ijikọta usoro izugbe nke BS EN 10217-1 na ihe achọrọ pụrụ iche nke BS EN 10217-3, enwere ike ijikwa ịdị mma nke usoro dum nke paịpụ ígwè P355NH site na nhọrọ ihe ruo na nnabata ngwaahịa emechara. Mgbe ịzụrụ ihe, a na-atụ aro ka ị kwuo nke ọma ụdị ọkọlọtọ (dịka BS EN 10217-3:2002+A1:2005) na nkwekọrịta teknụzụ ndị ọzọ (dịka -50)℃ihe achọrọ maka mmetụta) n'ime nkwekọrịta ahụ.