1. Kukura uye Kuronga

Manufacturing Process: Inoshanda kune welded simbi mapaipi akadai se electric resistance welding (ERW) uye submerged arc welding (SAW).

Classification: Yakakamurwa muKirasi A (yekutanga nhanho) uye Kirasi B (yepamusoro nhanho) zvichienderana nekuomarara kwekuongorora. P355NH inowanzo endeswa seKirasi B.

2. General Delivery Conditions

Surface Hunhu: Hapana hurema hwakaita sekutsemuka uye kupeta. Slight oxide scale inobvumirwa (haisi kukanganisa kuongorora).

Kumaka: Pombi imwe neimwe yesimbi inofanira kunyorwa nenhamba yakajairwa, giredhi resimbi (P355NH), saizi, nhamba yevira, nezvimwewo (EN 10217-1).

Dimensional kushivirira (EN 10217-1)

Parameter	Kirasi B kushivirira zvinodiwa (inoshanda kuP355NH)	Nzira yekuedza (EN)
Kunze dhayamita (D)	±0.75% D kana±1.0mm (iyo yakakura kukosha)	EN ISO 8502
Kukora kwemadziro (t)	+10%/-5% t (t≤15mm)	Ultrasonic ukobvu kuyerwa (EN 10246-2)
Urefu	+100/-0 mm (kureba kwakatarwa)	Laser kutenderera

 

Yakakosha maitiro epaipi yeP355NH simbi pombi

1. Welding process control (EN 10217-3)

ERW simbi pombi:

Kurapa kwekupisa kwepamhepo kunodiwa mushure mepamusoro-frequency welding (induction heat kusvika 550 ~ 600℃uye kunonoka kutonhora).

Weld musono extrusion control:≤10% rusvingo ukobvu (kudzivisa fusion isina kukwana). 

SAW simbi pombi: 

Multi-waya welding (2 ~ 4 waya), kupisa kupinza≤35 kJ/cm (kudzivirira HAZ zviyo kukoromoka). 

1. Zvinotsanangurwa zvekurapa kwekupisa (EN 10217-3 + EN 10028-3)

Process	parameters	Chinangwa
Normalizing (N)	910±10℃×1.5min/mm, kutonhora kwemhepo	Natsa zviyo kusvika kuASTM 6 ~ 8 giredhi
Kuderedza Stress annealing (SR)	580~620℃×2min/mm, kutonhora kwevira (≤200℃/h)	Bvisa welding yakasara kushushikana

3. Nondestructive test (EN 10217-1 + EN 10217-3)

UT bvunzo:

Sensitivity:Φ3.2mm sandara pazasi gomba (EN ISO 10893-3). 

Kuvhara: 100% weld + 10mm zvinhu zvevabereki kumativi ese. 

Water pressure test: 

Test pressure = 2×inobvumirwa kushanda kumanikidza (zvishoma 20MPa, kumanikidza kubata≥15s).

Zvimwe zvinodiwa zvekushandisa zvakakosha

1. Kuoma kwekushisa kwepasi (-50℃)

Mamwe mazwi echibvumirano:

Impact simba≥60J (avhareji), muenzaniso mumwe chete≥45J (EN ISO 148-1). 

Shandisa Al+Ti composite deoxidation process kuderedza okisijeni.≤30ppm). 

2. High tembiricha kutsungirira simba (300℃)

Muedzo wekuwedzera:

10 ^ 5 maawa anokambaira kuputika simba≥150 MPa (ISO 204).

Yepamusoro tembiricha tensile data (Rp0.2@300℃≥300 MPa) inodiwa.

3. Corrosion resistance zvinodiwa

Optional process:

Inner wall shot peening (Sa 2.5 level, EN ISO 8501-1).

Rusvingo rwekunze rwakaputirwa neZn-Al alloy (150g/m², Annex B yeEN 10217-1).

Hunhu Zvinyorwa uye Chitupa (EN 10217-1)

Chitupa Chekuongorora:

TS EN 10204 3.1 Chitupa (simbi chirimwa chekuzviongorora) kana 3.2 Chitupa (chechitatu-bato retifiketi).

Inofanirwa kusanganisira: kuumbwa kwemakemikari, michina zvivakwa, NDT mhedzisiro, kupisa kurapwa curve.

Special marking:

Mapaipi ekupisa anodzika akanyorwa ne "LT" (-50℃). 

Mapombi ekupisa akanyorwa ne "HT" (+300℃).

Matambudziko akajairika uye mhinduro

Dambudziko Phenomenon	Chikonzero Ongororo	Zvigadziriso (Zvichienderana Nezviyero)
Kusakwana simba simba rewelds	zviyo zveHAZ zvakakora	gadzirisa welding heat input≤25 kJ/cm (EN 1011-2)
Hydraulic test leakage	Zvisizvo kutwasanuka muchina parameters	UT kuongororazve chikamu chese chepombi + yemuno radiographic kuongorora (EN ISO 10893-5)
Dimensional kutsauka (ovality)	Zvisizvo kutwasanuka muchina parameters	Kutwasanudzazve (EN 10217-1)

Nekubatanidza iwo akajairwa mazwi eBS EN 10217-1 neakakosha zvinodiwa zveBS EN 10217-3, kunaka kwemaitiro ese eP355NH simbi pombi kubva pakusarudzwa kwezvinhu kusvika kupedzwa kwekugamuchirwa kwechigadzirwa kunogona kudzora zvizere. Paunenge uchitenga, zvinokurudzirwa kutaura zvakajeka iyo yakajairwa vhezheni (yakadai seBS EN 10217-3:2002+A1:2005) uye zvimwe zvibvumirano zvehunyanzvi (senge -50℃mhedzisiro zvinodiwa) muchibvumirano.