Seamless steel tubes and seamless alloy steel tubes GB5310 P11 P5 P9 ASTM A53/A53M-2012

Short Description:

Seamless steel pipes and welded steel pipes for general purpose steam, water, gas and air lines in ASTM A53/A53M-2012 Standard.


Product Detail

Product Tags

Overview

Standard: ASTM A53/A53M-2012

Grade Group: GR.A,GR.B ,Etc

Thickness: 1 - 100 mm

Outer Diameter(Round): 10 - 1000 mm

Length: Fixed length or random length

Section Shape: Round

Place of Origin: China

Certification: ISO9001:2008

 

Alloy Or Not: not

Application: for force and pressure parts, but also for general purpose steam, water, gas and air pipes

Surface Treatment: As customer's requirement

Technique: Hot Rolled or Cold Rolled

Heat treatment: Annealing/Normalizing/Stress Relieving

Special Pipe: Thick Wall Pipe

Usage: for force and pressure parts, for general purpose

Test: ECT/UT

Application

It Is Mainly Used for force and pressure parts, and for general purpose steam, water, gas and air pipes.

Main Grade

GR.A, GR.B

Chemical Component

Grade

 Component %,≤
C Mn P S

    CuA

  NiA

CrA

MoA VA
S type(seamless pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
E type(Resistance welded pipe)
GR.A 0.25B 0.95 0.05 0.045

0.40

0.40

0.40

0.15 0.08
GR.B 0.30C 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08
F type(Furnace Welded Pipe)
A 0.30B 1.20 0.05 0.045

0.40

0.40

0.40

0.15 0.08

A The sum of these five elements must not be greater than 1.00%。

B For every 0.01% decrease in the maximum carbon content, the maximum manganese content is allowed to increase by 0.06%, but the maximum cannot exceed 1.35%.

C Each 0.01% decrease in the maximum carbon content will allow the maximum manganese content to increase by 0.06%, but the maximum must not exceed 1.65%.

Mechanical Property

item GR.A GR.B

tensile strength, ≥, psi [MPa]

Yield Strength, ≥, psi [MPa]

Gauge 2in.or 50mm elongation

48 000 [330]30 000 [205]A,B 60 000 [415]35 000 [240]A,B

A The minimum elongation of gauge length 2in. (50mm) shall be determined by the following formula:

e=625000(1940)A0.2/U0.9

e = the minimum elongation of the gauge 2in. (50mm), the percentage rounded to the nearest 0.5%;

A = Calculated according to the specified outer diameter of the nominal tube or the nominal width of the tensile sample and its specified wall thickness, and rounded to the nearest cross-sectional area of the tensile sample of 0.01 in.2 (1 mm2), and It is compared with 0.75in.2 (500mm2), whichever is smaller.

U = specified minimum tensile strength, psi (MPa).

B For various combinations of different sizes of tensile test specimens and prescribed minimum tensile strength, the required minimum elongation is shown in Table X4.1 or Table X4.2, according to its applicability.

Test Requirement

Tensile test, bending test, hydrostatic test, nondestructive electrical test of welds.

Supply Ability

Supply Ability: 2000 Tons Per Month Per Grade Of ASTM A53/A53M-2012 Steel Pipe

Packaging

In Bundles And In Strong Wooden Box

Delivery

7-14 days if in stock, 30-45 days to produce

Payment

30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight

Product Detail


  • Previous:
  • Next:

  • Write your message here and send it to us