Seamless Steel Tubes For Petroleum Cracking,GB9948-2006,Sanon Pipe

Short Description:

As we all know, fuel oil is refined from petroleum. The price of petroleum is rising these years, and the cost of driving is getting higher and higher. In the process of extracting oil, many pipelines need to be installed.

Here’s a look at the pipeline:

Tubing (GB9948-88) is a seamless steel tube suitable for furnace tube, heat exchanger and pipeline in petroleum refinery.

Steel pipe for geological drilling (YB235-70) is used for core drilling by geological department, which can be divided into drill pipe, drill collar, core pipe, casing pipe and precipitation pipe according to its use.

Oil pipe is a kind of long steel with hollow section and no joint around, while petroleum cracking pipe is a kind of economic section steel.

Tubing is widely used in the manufacture of structural and mechanical parts such as oil drill pipes, car drive shafts, bicycle frames and steel scaffolding for moving pictures in construction. Using petroleum cracking tube to manufacture ring parts can improve material utilization rate, simplify manufacturing process, save material and processing time, such as rolling bearing ring, jack sleeve, etc., has been widely used to manufacture steel pipe. Petroleum cracking tube or a variety of conventional weapons indispensable material, barrel, barrel and so on to petroleum cracking tube to manufacture. Petroleum cracking pipe can be divided into round pipe and special-shaped pipe according to the shape of cross-sectional area. Since the area of petroleum cracking pipe is the largest with the same perimeter, more fluid can be transported with circular pipe.

High quality carbon structural steel grades are 20g, 

20mng and 25mng;Alloy structural steel grades: 15mog, 20mog, 12crmog,15CrMoG、12Cr2MoG、12CrMoVG,etc


  • Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight
  • Min.Order Quantity: 1 PC
  • Supply Ability: Annual 20000 Tons Inventory of Steel Pipe
  • Lead Time: 7-14 days if in stock, 30-45 days to produce
  • Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.
  • Product Detail

    15Crmo

    Product Tags

    Overview

    Standard: GB9948-2006 Heat Treatment: Annealing/normalizing/Tempering
    Grade Group: 10、12CrMo、15CrMo, 07Crl9Nil0, etc Outer Diameter(Round): 10 - 1000 Mm
    Thickness: 1 - 100 mm Application: heat exchange tubes
    Outer Diameter(Round): 10 - 1000 mm Surface Treatment: As Customer's Requirement
    Length: Fixed length or random length Technique: Hot Rolled
    Section Shape: Round Special Pipe: Thick Wall Pipe
    Place of Origin: China Usage: heat exchange tubes
    Certification: ISO9001:2008 Test:UT/MT

    Application

    Seamless steel tubes for petroleum cracking are applicable to seamless steel tubes for furnace tubes, heat exchange tubes and pressure pipes in petrochemical industry.

    High quality carbon structural steel grades are 20g, 20mng and 25mng.
    Alloy structural steel grades: 15mog, 20mog, 12crmog
    15CrMoG、12Cr2MoG、12CrMoVG, etc

    Main Grade

    Grade of high-quality carbon structural steel:  10#20#

    High quality carbon structural steel grades : 20g, 20mng and 25mng

    Alloy structural steel grades: 15mog, 20mog, 12crmog, 15CrMoG、12Cr2MoG,etc

    Chemical Component

    No Grade Chemical Component %
    C Si Mn Cr Mo Ni Nb Ti V Cu P S
    High Quality Carbon Structural Steel 10 0. 07-0.13 0.17 -0. 37 0.35 -0.65 <0.15 <0.15 <0. 25 <0. 08 <0. 20 0. 025 0. 015
    20 0.17-0. 23 0.17 -0. 37 0.35 -0.65 <0. 25 <0.15 <0. 25 <0. 08 <0. 20 0. 025 0. 015
    Alloy Structural Steel 12CrMo 0. 08-0.15 0.17 -0.37 0. 40-0. 70 0. 40-0. 70 0. 40 -0.55 <0. 30 <0. 20 0. 025 0. 015
    15CrMo 0.12 -0.18 0.17-0. 37 0.40 -0. 70 0. 80-1.1 0. 40-0.55 <0. 30 <0. 20 0. 025 0. 015
    12CrlMo 0. 08 -0.15 0.50 -1. 00 0. 30-0.6 1.00-1. 50 0.45 -0.65 <0. 30 <0, 20 0. 025 0. 015
    12CrlMoV 0. 08-0.15 0.17-0. 37 0. 40-0. 70 0.90-1.2 0. 25 -0.35 <0. 30 0.15 -0. 30 <0. 20 0.025 0. 010
    12Cr2Mo 0.08-0.15 <0. 50 0. 40-0. 60 2. 00-2. 50 0. 90-1.13 <0. 30 <0. 20 0. 025 0. 015
    12Cr5MoI <0.15 <0. 50 0.30-0.6 4. 00-6 0. 45 -0. 60 <0. 60   <0. 20 0. 025 0. 015
    12Cr5MoNT
    12Cr9MoI <0.15 0. 25-1. 00 0. 30-0. 60 8.00 -10. 00 0. 90-1.1 <0. 60 <0. 20 0. 025 0, 015
    12Cr9MoNT
    Stainless Heat Resistant Steel 07Crl9Nil0 0. 04-0.1 <1. 00 <2. 00 18. 00-20. 00 8. 00-11 0. 030 0. 015
    07Crl8NillNb 0. 04-0.1 <1. 00 <2. 00 17. 00-19. 00 9.00-12. 00 8C-1.1 0. 030 0. 015
    07Crl9NillTi 0. 04-0.1 <0. 75 <2. 00 17.00-20. 00 9. 00~13. 00 4C-0. 60 0.03 0. 015
    022Crl7Nil2Mo2 <0. 030 <1. 00 <2. 00 16. 00-18. 00 2. 00-3. 00 10. 00 -14. 00 0.03 0. 015

    Mechanical Property

     No Tensile
    MPa
    Yield
    MPa
    Elong after fracture A/% Shork absorption energy kv2/j Brinell hardness number
    portrait transver portrait transver
    not less than no more than
    10 335〜475 205 25 23 40 27  
    20 410〜550 245 24 22 40 27  
    12CrMo 410〜560 205 21 19 40 27 156 HBW
    15CrMo 440〜640 295 21 19 40 27 170 HBW
    12CrlMo 415〜560 205 22 20 40 27 163 HBW
    12CrlMoV 470〜640 255 21 19 40 27 179 HBW
    12Cr2Mo 450~600 280 22 20 40 27 163 HBW
    12Cr5MoI 415〜590 205 22 20 40 27 163 HBW
    12Cr5MoNT 480〜640 280 20 18 40 27
    12Cr9MoI 460〜640 210 20 18 40 27 179 HBW
    12Cr9MoNT 590—740 390 18 16 40 27  
    O7Crl9NilO 2520 205 35     187 HBW
    07Crl8NillNb >520 205 35   187 HBW
    07Crl9NillTi >520 205 35 187 HBW
    022Crl7Nil2Mo2 >485 170 35 187 HBW
    For steel with wall thickness less than 5mm tube do not make hardness experiment

     

    Test Requirement

    Hydraulic test
    Hydraulic test shall be carried out for steel pipes one by one. The maximum test pressure is 20 MPa. Under the test pressure, the stabilization time shall not be less than 10 s, and leakage of steel pipe is not allowed.
    Flattening test
    Flattening test shall be conducted for steel pipe with outer diameter greater than 22 mm
    Flaring test
    High quality carbon structural steel and stainless (heat-resistant) steel pipes with an outer diameter of not more than 76 mm and a wall thickness of not more than 8 mm shall be subject to expanding test. The flaring test shall be carried out at room temperature. The outer diameter flaring rate of the sample after the top core taper is 60% of the flaring shall meet the requirements of table 7. No cracks or cracks are allowed on the sample after the flaring. According to the requirements of the demander and noted in the contract, the alloy structural steel can also be used for expanding test.
    Nondestructive teste
    The steel pipes shall be subject to ultrasonic flaw detection one by one in accordance with the provisions of GB / T 5777-2008. According to the requirements of the demander, other non-destructive tests can be added after negotiation between the supplier and the demander and indicated in the contract.
    Intergranular corrosion test
    Intergranular corrosion test shall be conducted for stainless (heat-resistant) steel pipe. The test method shall be in accordance with the provisions of Chinese method E in GB / T 4334-2008, and intergranular corrosion tendency is not allowed after the test.
    After negotiation between the supplier and the demander, and noted in the contract, the demander can designate other corrosion test methods.

    Product Detail


  • Previous:
  • Next:

  • Oil, petrochemical, high pressure boiler, special use of seamless tube boiler seamless tube, geological seamless steel tube and oil seamless tube.

    Chemical Component

    brand Chemical Component(%)
      C Mn Si Cr Mo Ni Nb+Ta S P
    15CrMo 0.12~0.18 0.40~0.70 0.17~0.37 0.80~1.10 0.40~0.55 ≤0.30 _ ≤0.035 ≤0.035

    Mechanical Property

    brand Tensile
    MPa
    Yield
    MPa
    Elongation(%)
    15CrMo 440~640 295 22

    mmexport1652670379253.jpg