Seamless Medium carbon steel boiler and Superheat tubes ASTM A210 standard

Short Description:

SA210 High Pressure Alloy Pipe Implementation Standard ASTM A210—– ASME SA210- American Society Of Mechanical Engineers Standard.

Suitable For Use In Boiler Pipe And Flue Pipe, Including Safety End, Vault And Support Pipe And Superheater Pipe With Minimum Wall Thickness Seamless Medium Carbon Steel Pipe.

Main Production Of High Pressure Alloy Pipe Grades: A210A1, A210C And So On.


  • Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight
  • Min.Order Quantity: 20T
  • Supply Ability: Annual 20000 Tons Inventory of Steel Pipe
  • Lead Time: 7-14 days if in stock, 30-45 days to produce
  • Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.
  • Product Detail

    Product Tags

    Overview

    Standard: ASTM SA210 Alloy Or Not: Carbon steel
    Grade Group: GrA. GrC Application: Boiler Pipe
    Thickness: 1 - 100 mm Surface Treatment: As customer's requirement
    Outer Diameter(Round): 10 - 1000 mm Technique: Hot Rolled/Cold Drawn
    Length: Fixed length or random length Heat treatment: Annealing/normalizing
    Section Shape: Round Special Pipe: Thick Wall Pipe
    Place of Origin: China Usage: Boiler and Heat Exchanger
    Certification: ISO9001:2008 Test: ET/UT

     

    Application

    It is mainly used to make high-quality seamless carbon steel, for boiler pipes, super heat pipes

    for bolier industry , heat changer pipe etc. With difference sizes and thickness

    Main Grade

    Grade of high-quality carbon boiler steel: GrA, GrC

    Chemical Component

    Element Grade A Grade C
    C ≤0.27 ≤0.35
    Mn ≤0.93 0.29-1.06
    P ≤0.035 ≤0.035
    S ≤0.035 ≤0.035
    Si ≥ 0.1 ≥ 0.1

    A For each reduction of 0.01 % below the specified carbon maximum, an increase of 0.06 % manganese above the specified maximum will be permitted up to a maximum of 1.35 %.

    Mechanical Property

      Grade A Grade C
    Tensile Strength ≥ 415 ≥ 485
    Yield Strength ≥ 255 ≥ 275
      Elongation rate ≥ 30 ≥ 30

     

    Test Requirement

    Hydraustatic Test:

    The Steel Pipe Should Be Tested Hydraulically One By One. The Maximum Test Pressure Is 20 MPa. Under The Test Pressure, The Stabilization Time Should Be Not Less Than 10 S, And The Steel Pipe Should Not Leak.

    After The User Agrees, The Hydraulic Test Can Be Replaced By Eddy Current Testing Or Magnetic Flux Leakage Testing.

    Flattening Test:

    Tubes With An Outer Diameter Greater Than 22 Mm Shall Be Subjected To A Flattening Test. No Visible Delamination, White Spots, Or Impurities Should Occur During The Entire Experiment.

    Flaring Test:

    According To The Requirements Of The Purchaser And Stated In The Contract, The Steel Pipe With Outer Diameter ≤76mm And Wall Thickness ≤8mm Can Be Done Flaring Test . The Experiment Was Performed At Room Temperature With A Taper Of 60 °. After The Flaring, The Flaring Rate Of The Outer Diameter Should Meet The Requirements Of The Following Table, And The Test Material Must Not Show Cracks Or Rips

    Hardness Test:

    Brinell or Rockwell hardness tests shall be made on specimens from two tubes from each lot