ASME SA-106/SA-106M-2015 Carbon steel pipe

Short Description:

Seamless carbon steel tube for high temperature


Product Detail

Product Tags

Overview

Standard: ASTM SA106 Alloy Or Not: Not
Grade Group: GR.A,GR.B,GR.C etc Application: Fluid Pipe
Thickness: 1 - 100 mm Surface Treatment: As customer's requirement
Outer Diameter(Round): 10 - 1000 mm Technique: Hot Rolled
Length: Fixed length or random length Heat treatment: Annealing/normalizing
Section Shape: Round Special Pipe: High temperature
Place of Origin: China Usage: Construction, Fluid Transportation
Certification: ISO9001:2008 Test: ECT/CNV/NDT

Application

 Seamless steel pipe for high temperature operation ASTM A106, suitable for high temperature,It is widely used in petroleum, chemical industry, boiler, power station, ship, machinery manufacturing, automobile, aviation, aerospace, energy, geology, construction and military industry and other industries.

oil pipe
石油行业1
oil pipe
106.1
106.2
106.3

Main Grade

Grade of high-quality carbon structural steel: GR.A,GR.B,GR.C

Chemical Component

 

  Composition, %
Grade A Grade B Grade C
Carbon, max 0.25A 0.3B 0.35B
Manganese 0.27-0.93 0.29-1.06 0.29-1.06
Phosphorus, max 0.035 0.035 0.035
Sulfur, max 0.035 0.035 0.035
Silicon, min 0.10 0.10 0.10
Chrome, maxC 0.40 0.40 0.40
Copper, maxC 0.40 0.40 0.40
Molybdenum, maxC 0.15 0.15 0.15
Nickel, maxC 0.40 0.40 0.40
Vanadium, maxC 0.08 0.08 0.08
A For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.
B Unless otherwise specified by the purchaser, for each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.65%.
C These five elements combined shall not exceed 1%.

Mechanical Property

    Grade A Grade B Grade C
Tensile strength, min, psi(MPa) 48 000(330) 60 000(415) 70 000(485)
Yield strength, min, psi(MPa) 30 000(205) 35 000(240) 40 000(275)
  Longitudinal Transverse Longitudinal Transverse Longitudinal Transverse
Elongation in 2 in. (50 mm), min, %
Basic minimum elongation transverse strip tests, and for all small sizes tested in full section
35 25 30 16.5 30 16.5
When standard round 2-in. (50-mm) gauge length test specimen is used 28 20 22 12 20 12
For longitudinal strip tests A   A   A  
For transverse strip tests, a deduction for each 1/32-in. (0.8-mm) decrease in wall thickness below 5/16 in. (7.9 mm) from the basic minimum elongation of the following percentage shall be made   1.25   1.00   1.00
A The minimum elongation in 2 in. (50 mm) shall be determined by the following equation:
e=625000A 0.2 / U 0.9
for inch-pound units, and
e=1940A 0.2 / U 0.9
for SI units,
where:
e = minimum elongation in 2 in. (50 mm), %, rounded to the nearest 0.5%,
A = cross-sectional area of the tension test specimen, in.2 (mm2), based upon specified outside diameter or nominal specified outside diameter or nominal specimen width and specified wall thickness, rounded to the nearest 0.01 in.2 (1 mm2). (If the area thus calculated is equal to or greater than 0.75 in.2 (500 mm2), then the value 0.75 in.2 (500 mm2) shall be used.), and
U = specified tensile strength, psi (MPa).

Test Requirement

In addition to ensuring chemical composition and mechanical properties, hydrostatic tests are performed one by one, and flaring and flattening tests are performed. . In addition, there are certain requirements for the microstructure, grain size, and decarburization layer of the finished steel pipe.

Supply Ability

Supply Ability: 1000 Tons Per Month Per Grade of ASTM SA-106 Steel Pipe

Packaging

In Bundles And In Strong Wooden Box

Delivery

7-14 days if in stock, 30-45 days to produce

Payment

30% depsoit, 70% L/C or B/L copy   or  100% L/C at sight