1. Kuchuluka ndi Magulu

Njira Yopangira: Imagwiritsidwa ntchito pamapaipi achitsulo opangidwa ndi welded monga electric resistance welding (RW) ndi kumizidwa arc kuwotcherera (SAW).

Magulu: Amagawidwa mu Gulu A (mulingo woyambira) ndi Gulu B (wotsogola) molingana ndi kukhwima kwa kuwunika. P355NH nthawi zambiri imaperekedwa ngati Gulu B.

2. Zoyenera Kuperekera Zonse

Ubwino Wapamwamba: Palibe zolakwika monga ming'alu ndi mapindikidwe. Pang'ono oxide sikelo amaloledwa (sakhudza kuyendera).

Kuyika: Chitoliro chilichonse chachitsulo chiyenera kulembedwa ndi nambala yokhazikika, kalasi yachitsulo (P355NH), kukula, nambala ya ng'anjo, etc. (EN 10217-1).

Kulekerera kwa Dimensional (EN 10217-1)

Parameter	Zofunikira zololera za Mkalasi B (zogwirizana ndi P355NH)	Njira yoyesera (EN)
M'mimba mwake (D)	±0.75% D kapena±1.0mm (mtengo wokulirapo)	EN ISO 8502
Makulidwe a khoma (t)	+ 10%/-5% t (t≤15 mm)	Muyeso wa makulidwe a Ultrasonic (EN 10246-2)
Utali	+ 100/-0 mm (utali wokhazikika)	Kusintha kwa laser

 

Tsatanetsatane wofunikira wa chitoliro chachitsulo cha P355NH

1. Kuwongolera njira zowotcherera (EN 10217-3)

ERW chitoliro chachitsulo:

Kutentha kwapaintaneti kumafunika pambuyo pakuwotcherera kwanthawi yayitali (kutentha kolowera mpaka 550 ~ 600℃ndi kuzizira pang'onopang'ono).

Weld seam extrusion control:≤10% makulidwe a khoma (kupewa kuphatikizika kosakwanira). 

Chitoliro chachitsulo cha SAW: 

Mipikisano waya kuwotcherera (2 ~ 4 mawaya), zolowetsa kutentha≤35 kJ/cm (kupewa HAZ tirigu coarsening). 

1. Zofunikira pakuwongolera kutentha (EN 10217-3 + EN 10028-3)

Njira	magawo	Cholinga
Normalizing (N)	910±10℃ ×1.5min/mm, kuziziritsa kwa mpweya	Yengani mbewuzo mpaka ASTM 6-8 giredi
Kuchepetsa Kupsinjika Maganizo (SR)	580-620℃ ×2min/mm, kuzirala kwa ng'anjo (≤200℃/h)	Chotsani kuwotcherera kupsinjika kotsalira

3. Kuyesa kosawonongeka (EN 10217-1 + EN 10217-3)

Kuyesa kwa UT:

Kukhudzika:Φ3.2mm lathyathyathya pansi dzenje (EN ISO 10893-3). 

Kuphimba: 100% weld + 10mm makolo zinthu mbali zonse. 

Kuyeza kuthamanga kwa madzi: 

Kuthamanga kwa mayeso = 2×kukakamizidwa kovomerezeka (osachepera 20MPa, kukakamiza kugwira≥15s).

Zofunikira zowonjezera pamapulogalamu apadera

1. Kutentha kochepa kumakhudza kulimba (-50℃)

Mgwirizano wowonjezera:

Mphamvu yamphamvu≥60J (avareji), chitsanzo chimodzi≥45J (EN ISO 148-1). 

Gwiritsani ntchito njira yophatikizira ya Al+Ti kuti muchepetse mpweya wa okosijeni (≤30 ppm). 

2. Mphamvu yopirira kutentha kwambiri (300℃)

Mayeso owonjezera:

10 ^ 5 maola kukwawa kuphulika mphamvu≥150 MPa (ISO 204).

Kutentha kwakukulu kwa data (Rp0.2@300℃≥300 MPa) ndiyofunikira.

3. Zofunikira za kukana kwa dzimbiri

Njira yosankha:

Mkati khoma kuwombera peening (Sa 2.5 mlingo, EN ISO 8501-1).

Khoma lakunja limakutidwa ndi aloyi ya Zn-Al (150g/m², Zowonjezera B za EN 10217-1).

Zolemba Zapamwamba ndi Chitsimikizo (EN 10217-1)

Satifiketi Yoyendera:

TS EN 10204 3.1 Satifiketi (yodziyesa yokha) kapena 3.2 Satifiketi (chitsimikizo cha chipani chachitatu).

Ayenera kuphatikizapo: mankhwala zikuchokera, makina katundu, NDT zotsatira, kutentha pamapindikira.

Zolemba zapadera:

Mapaipi otsika kwambiri amalembedwa ndi "LT" (-50℃). 

Mapaipi otentha kwambiri amalembedwa ndi "HT" (+300℃).

Mavuto wamba ndi njira zothetsera

Vuto Phenomenon	Chifukwa Analysis	Zothetsera (Zotengera Miyezo)
Mphamvu zosakwanira za welds	mbewu za HAZ	sinthani kutentha kwa kuwotcherera≤25 kJ/cm (EN 1011-2)
Kutaya kwa hydraulic test	Zolakwika makina owongola magawo	UT kuyang'ananso gawo lonse la chitoliro + kuyang'ana kwa radiographic mdera lanu (EN ISO 10893-5)
Dimensional kupatuka (ovality)	Zolakwika makina owongola magawo	Kuwongolanso (EN 10217-1)

Kuphatikiza mawu wamba a BS EN 10217-1 ndi zofunikira zapadera za BS EN 10217-3, mtundu wa njira yonse ya P355NH chitoliro chachitsulo kuchokera pakusankha zinthu mpaka kuvomereza komaliza kumatha kuwongoleredwa kwathunthu. Pogula, tikulimbikitsidwa kunena momveka bwino mtundu wamba (monga BS EN 10217-3:2002+A1:2005) ndi mapangano owonjezera aukadaulo (monga -50℃zotsatira zofunika) mu mgwirizano.